- SABIC Innovative Plastics Lexan® FXD2034 PC (Europe-Africa-Middle East)
SABIC Innovative Plastics Lexan® FXD2034 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXD2034 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LEXAN FXD2034 is a translucent medium viscosity flame retardant grade for light diffusion applications. The material is UV-stabilized. Can meet I2 rating according NF F16101.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 145 °C | 293 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D-6606 BLK
- Network Polymers MS 130HF Styrene Methyl Methacrylate Terpolymer
- SABIC Innovative Plastics Lexan® PPC4704 PPC (Asia Pacific)
- Garlock 505 CPE Sheet Rubber
- Taiwan PU Corporation TPUI-L70 Low Temperature Resistance, Injection Molding Polyester Base TPU
- Taiwan Sheen Soon Sheenthane® A8820N Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics Xenoy® FXX210SK PBT+PC (Europe-Africa-Middle East)
- Stellarchem 8075 TPE Compound
- Hexcel® HexForce™ GA080 Carbon Fabric
Copyright © lookpolymers.com All Rights Reserved