PolyOne Edgetek® PS-1000 Polybutylene Terephthalate (PBT) (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PS-1000 Polybutylene Terephthalate (PBT)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:UL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 55.2 MPa | 8000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.800 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 81.0 µm/m-°C @Temperature 20.0 °C |
45.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | Molding |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | |
| Drying Temperature | 104 °C | 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Oxford Polymers PC 20 Unfilled Polycarbonate for Injection Molding
- Kolon SPESIN® KP212VO Flame Retardant PBT Resin (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP KFL34XXC Acetal Copolymer (Europe-Africa-Middle East)
- Solvay TECHNYL® C 246SI V11 PA6, 11% glass filled, DRY
- SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6
- DuPont Performance Polymers Hytrel® 40CB Polyester Elastomer TPC-ET (Unverified Data**)
- BASF Ultradur S 4090 G4 20% Glass Filled PBT
- ATI Allegheny Ludlum AL 13-8™ H 1025 Precipitation Hardening Alloy
Copyright © lookpolymers.com All Rights Reserved