PolyOne Edgetek® ATH-10CF/000 Acetal-Homopolymer, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ATH-10CF/000 Acetal-Homopolymer, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm |
0.10 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 227 °C | 400 - 440 °F | Molding |
| Mold Temperature | 65.6 - 71.1 °C | 150 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyOne Geon™ Specialty Suspension Impel S100 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 8% Plasticizer (discontinued **)
- Trelleborg Emerson & Cuming Stycast® TU-906 Two-Component Polyurethane Flexible Encapsulant
- Epoxy Technology EPO-TEK® 302-3M Optically Transparent Epoxy
- 3M PS195 White Yupo™ TIS Label Products
- Beijing Ranger Chem PBT-201-G30 211 Flame Retarding FR PBT
- Polimeri Europa Koblend PD P 479 Polystyrene-Polyolefin Alloy (discontinued **)
- Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved