3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in the manufacture and repair of furniture, cabinets, and other wood products.Information provided by 3M
Physical Properties Metric English Comments
Viscosity >= 2250 cP
>= 2250 cP
Mechanical Properties Metric English Comments
Shear Strength 1.72 MPa
250 psi
Overlap, Particleboard, Substrate Failure
2.76 MPa
400 psi
Overlap, MDF, Cohesive Failure
2.76 MPa
400 psi
Overlap, Melamine, Substrate Failure
4.14 MPa
600 psi
Overlap, Polyurethane Finish, Adhesive Failure
4.83 MPa
700 psi
Overlap, Pine, Substrate/Cohesive Failure
5.17 MPa
750 psi
Overlap, Polyacrylic Finish, Cohesive Failure
6.21 MPa
900 psi
Overlap, High Pressure Laminate, Substrate Failure
7.24 MPa
1050 psi
Overlap, Plywood, Cohesive Failure
9.31 MPa
1350 psi
Overlap, Poplar, Substrate/Cohesive Failure
9.31 MPa
1350 psi
Overlap, Maple, Substrate Failure
16.5 MPa
2400 psi
Overlap, Oak, Substrate/Cohesive Failure
18.6 MPa
2700 psi
Overlap, Aluminum, Adhesive Failure
19.7 MPa
2850 psi
Overlap, Steel, Adhesive Failure
0.758 MPa

@Temperature 66.0 °C
110 psi

@Temperature 151 °F
Overlap, Polyurethane Finish, Adhesive Failure
3.79 MPa

@Temperature 32.0 °C
550 psi

@Temperature 89.6 °F
Overlap, Polyurethane Finish, 90% RH, Adhesive Failure
4.14 MPa

@Temperature 32.0 °C
600 psi

@Temperature 89.6 °F
Overlap, Pine, 90% RH, Adhesive Failure
4.83 MPa

@Temperature 66.0 °C
700 psi

@Temperature 151 °F
Overlap, Plywood, Substrate Failure
5.86 MPa

@Temperature 32.0 °C
850 psi

@Temperature 89.6 °F
Overlap, Aluminum, 90% RH, Adhesive Failure
6.55 MPa

@Temperature 66.0 °C
950 psi

@Temperature 151 °F
Overlap, Pine, Adhesive Failure
7.24 MPa

@Temperature 32.0 °C
1050 psi

@Temperature 89.6 °F
Overlap, Plywood, 90% RH, Substrate Failure
12.4 MPa

@Temperature 32.0 °C
1800 psi

@Temperature 89.6 °F
Overlap, Oak, 90% RH, Substrate/Adhesive Failure
13.1 MPa

@Temperature 66.0 °C
1900 psi

@Temperature 151 °F
Overlap, Oak, Substrate/Adhesive Failure
13.8 MPa

@Temperature 66.0 °C
2000 psi

@Temperature 151 °F
Overlap, Aluminum, Adhesive Failure
Processing Properties Metric English Comments
Cure Time 1440 min
24.0 hour
Full Cure
Descriptive Properties Value Comments
Appearance Clear-Slightly yellow liquid