- PolyOne Edgetek® AT-10GB/000 Black Acetal-Copolymer, Glass Bead Filled (discontinued **)
PolyOne Edgetek® AT-10GB/000 Black Acetal-Copolymer, Glass Bead Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AT-10GB/000 Black Acetal-Copolymer, Glass Bead Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.17 mm |
0.20 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.021 cm/cm | 0.021 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed, 0.062 in bars; ASTM D648 |
| Flammability, UL94 | HB | HB | Black; 0.062 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 °C | 400 °F | Molding |
| Mold Temperature | 54.4 - 76.7 °C | 130 - 170 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
Users viewing this material also viewed the following:
- ND Industries SuperGlue Ethyl 309
- Styrolution PS 2610 GPPS
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
- Trelleborg Sealing Solutions HiMod® 914 Thermoplastic Bearing
- American Elements Copper Nanoparticles
- ELASTO UK Dryflex® 600550S SEBS Based Material, Filled Qualities, 55A Hardness, Natural
- Arlon 0.030" (0.762 mm) Silicone Traction Motor Insulation with Fiberglass Substrate (19220R030)
- Techmer ES Luriblend® PPA GF30 TL15 30% Glass Filled
- Gouda Vuurvast ADHESIET 170 P Dry Air-Setting Refractory Mortar
Copyright © lookpolymers.com All Rights Reserved