DuPont™ HPF® 2000 Amorphous Polymer for Golf Balls

Category	Polymer
Manufacturer	DuPont
Trade Name	HPF®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ HPF® 2000 Amorphous Polymer for Golf Balls.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DuPont™ HPF 2000 offers high COR and lower compression. This combination of properties makes it extremely versatile and possible for this polymer to be used as a core, mantle, or cover in a golf ball construction. DuPont™ HPF 2000 offers a combination of high resilience and low compression. This polymer is a highly amorphous material.

Physical Properties	Metric	English	Comments
Density	0.960 g/cc	0.0347 lb/in³	ASTM D792, ISO 1183
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55	55	ASTM D2240
Tensile Strength	13.0 MPa	1890 psi	ASTM D638
Elongation at Break	330 %	330 %	ASTM D638
Flexural Modulus	0.0860 GPa	12.5 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	73.0 °C	163 °F	ASTM D3418, ISO 3146
Vicat Softening Point	54.0 °C	129 °F	ASTM D1525, ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	<= 285 °C	<= 545 °F