PolyOne Edgetek® AS-13CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-13CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm - 1e+05 | 100 ohm-cm - 1e+05 | ASTM D257 |
| Surface Resistivity per Square | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 249 °C | 430 - 480 °F | Molding |
| Mold Temperature | 54.4 - 65.6 °C | 130 - 150 °F | |
| Drying Temperature | 54.4 °C | 130 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GB 1200 20 HS BLACK 18 Polyamide 66 (Nylon 66)
- LG Chemical HF380NS ABS, High Flow, General Anti-Static
- Sylvin Technologies 9980-95 Natural PVC Molding Compound
- Techmer ES Statiblend® PA6 GF30 AS BK 30% Glass Filled
- Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS
- Borealis Beta (ß)-PP™ BE60-7032 Grey Polypropylene Homopolymer for Pressure Pipes, Fittings and Sheets
- Wellman Wellamid® GS40-60 42L-N 40% Glass Sphere Filled Nylon 6, Lubricated
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
Copyright © lookpolymers.com All Rights Reserved