- Owens Corning Glass Fiber Reinforced Polyester, Woven Roving (Lay-up), 50 wt.% glass
Owens Corning Glass Fiber Reinforced Polyester, Woven Roving (Lay-up), 50 wt.% glass
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Polyester, Woven Roving (Lay-up), 50 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 50 | 50 | |
| Tensile Strength, Ultimate | 260 MPa | 37700 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Modulus of Elasticity | 15.5 GPa | 2250 ksi | ASTM D638 |
| Flexural Strength | 320 MPa | 46400 psi | ASTM D790 |
| Flexural Modulus | 15.5 GPa | 2250 ksi | ASTM D790 |
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 |
| Izod Impact, Notched | 18.0 J/cm | 33.7 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.20 µm/m-°C @Temperature 20.0 °C |
4.00 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 60 Hz |
4.2 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJJC310L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F)
- SABIC Innovative Plastics LNP THERMOCOMP DFZ22P PC
- ELASTO UK Dryflex® 660500S SEBS Based Material, Semi-Filled Qualities, 50A Hardness, Natural
- Axion Polymers Axpoly® PP06 5001 Enhanced Black General Purpose Polypropylene
- Aremco Ceramacast™ 510 High Temperature Potting & Casting Material Alumina
Copyright © lookpolymers.com All Rights Reserved