PlastiComp Complet® LGF40 - PA66 MT Nylon 66, 40% Long Glass Fiber Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LGF40 - PA66 MT Nylon 66, 40% Long Glass Fiber Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 40% long glass fiber reinforcementImpact modifiedInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D-792 |
| Filler Content | 40 % | 40 % | Long Glass Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 207 MPa | 30000 psi | ASTM D-638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D-638 |
| Tensile Modulus | 13.793 GPa | 2000.5 ksi | ASTM D-638 |
| Flexural Strength | 297 MPa | 43100 psi | ASTM D-790 |
| Flexural Modulus | 9.655 GPa | 1400 ksi | ASTM D-790 |
| Izod Impact, Notched | 3.95 J/cm | 7.40 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 16.02 J/cm | 30.01 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Middle Barrel Temperature | 288 - 304 °C | 550 - 580 °F | |
| Front Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Nozzle Temperature | 288 - 304 °C | 550 - 580 °F | |
| Melt Temperature | 293 - 310 °C | 560 - 590 °F | |
| Mold Temperature | 93.3 °C | 200 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 85.0 °C @Time 14400 sec |
185 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.18 % | <= 0.18 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |
Users viewing this material also viewed the following:
- Mytex Polymers 1391 Polypropylene, Non-filled, Compounded
- LG Chemical Lupoy 3010-22 Polycarbonate Resin
- Lucite International Diakon® CRG812 Acrylic Polymer, Toughened Compound
- Lehmann & Voss LUVOCOM® NY-4/PL/15/BK Polyamide 612, with PTFE
- SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK
- Teknor Apex APEX® 90-A471R-85-NT Polyvinyl Chloride, Flexible
- Zeon Chemicals Nipol® 1094-80 Nitrile Elastomer
- Eastman Provista NXT Copolymer Resin for Profile Extrusion
- DSM Akulon® K240-HPG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Dry)
- Chosun Refractories HSC-16S-W2 Dense and High-Strength Castable, Credens
Copyright © lookpolymers.com All Rights Reserved