Plastcom SLOVAMID 6 HI/1 TLS PA6, improved strength

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID 6
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 HI/1 TLS PA6, improved strength.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6 with the content of thermoplastic kaoutchouc. Impacted, for mouldings with high toughness either at minus temperatures, suitable for external use, eg. ski shoes, sports and safety helmets, protection ledges of the car-doors. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
Viscosity Measurement 2.04 - 2.08
2.04 - 2.08
Linear Mold Shrinkage 0.0208 cm/cm
0.0208 in/in
Linear Mold Shrinkage, Transverse 0.0204 cm/cm
0.0204 in/in
Melt Flow 4.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
4.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
Elongation at Break 4.0 %
4.0 %
Tensile Modulus 2.25 GPa
326 ksi
Flexural Strength 73.0 MPa
10600 psi
Flexural Modulus 1.93 GPa
280 ksi
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
Charpy Impact, Notched 1.60 J/cm²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
3.70 J/cm²

@Temperature 23.0 °C
17.6 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 180 °C
356 °F
B
Flammability, UL94 HB
HB
Glow Wire Test 850 °C
1560 °F
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 50.0 - 60.0 °C
122 - 140 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Injection Pressure 80.0 - 150 MPa
11600 - 21800 psi