Permabond HH167 Anaerobic Retainer
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | Permabond |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Permabond HH167 Anaerobic Retainer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Permabond® HH167 is a high viscosity gap filling silver paste, which can be used for repairing metal machinery parts. It is ideal for repairing worn shafts, broken threads, damaged keyways and splines. Permabond HH167 has excellent chemical and temperature resistance. NB. This adhesive is only suitable for gaps
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 90000 cP @Temperature 25.0 °C |
90000 cP @Temperature 77.0 °F |
at 20 rpm vibration |
| 500000 cP @Temperature 25.0 °C |
500000 cP @Temperature 77.0 °F |
at 2rpm vibration | |
| Storage Temperature | 5.00 - 25.0 °C | 41.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 32.0 MPa | 4640 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 149 °C | 300 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 23.0 °C |
0.250 hour @Temperature 73.4 °F |
M10 steel, handling strength |
| 30.0 min @Temperature 23.0 °C |
0.500 hour @Temperature 73.4 °F |
Zinc, handling strength | |
| 60.0 min @Temperature 23.0 °C |
1.00 hour @Temperature 73.4 °F |
Aluminum, handling strength | |
| 180 - 360 min @Temperature 23.0 °C |
3.00 - 6.00 hour @Temperature 73.4 °F |
M10 steel, working strength | |
| 360 min @Temperature 23.0 °C |
6.00 hour @Temperature 73.4 °F |
Zinc, working strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
M10 steel, full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Silver | Uncured |
| Maximum Gap Fill (mm) | 0.5 | |
| Strength Retention | 50% at 150°C | Relative to 0°C |
| 80% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 32 | M10 steel, prevail |
| 45 | M10 steel, break | |
| UV Fluorescence | No | Uncured |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 5019
- Parker Chomerics Tecknit® 0002 Highly Conductive Adhesive-Sealant Silver Silicone
- Materion Beryllium Copper Alloy 25 Wire; 1/2H (TD02) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Gwent Electronic Materials C2070920D1 Depolymerisable Carbon Ink
- Mueller Alloy 3533 Dezincification Brass (UNS C35330)
- Saint-Gobain COHRlastic® 9235 High Performance Silicone Solid Rubber
- Formosa Plastics Formolene® HB5502F Blow Molding HDPE
- Covestro Makroblend® UT-620 G Polycarbonate + Polyester Blend
- Arkema Group OREVAC® 18350P Grafted Maleic Anhydride Polyethylene
- Axiall 3101 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved