Permabond A1042 Anaerobic Threadlocker

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond A1042 Anaerobic Threadlocker.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Permabond® A1042 is a rapid curing adhesive designed to lock and seal metal parts that subsequently may need to be dismantled for maintenance. The high vibration resistance makes Permabond A1042 particularly suited to replacing lock washers, split pins and other mechanical locking devices. The well proven chemical resistance of Permabond A1042 will reduce the effects of corrosion and make it suitable for sealing small hydraulic and pneumatic fittings. Features & Benefits: Rapid cure Vibration resistant Lubricates threads for easier assembly Provides corrosion protection WRAS listed for contact with wholesome (potable) waterInformation provided by Permabond.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Uncured
Viscosity	1700 cP @Temperature 25.0 °C	1700 cP @Temperature 77.0 °F	at 20 rpm vibration
	8000 cP @Temperature 25.0 °C	8000 cP @Temperature 77.0 °F	at 2 rpm vibration
Storage Temperature	5.00 - 25.0 °C	41.0 - 77.0 °F

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	12.0 MPa	1740 psi	steel collar and pin shear; ISO 10123

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F
Thermal Conductivity	0.190 W/m-K	1.32 BTU-in/hr-ft²-°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	11.0 kV/mm	279 kV/in

Processing Properties	Metric	English	Comments
Cure Time	4.98 min @Temperature 23.0 °C	0.0830 hour @Temperature 73.4 °F	M10 steel, handling strength
	4.98 min @Temperature 23.0 °C	0.0830 hour @Temperature 73.4 °F	Brass, handling strength
	15.0 min @Temperature 23.0 °C	0.250 hour @Temperature 73.4 °F	Brass, working strength
	30.0 min @Temperature 23.0 °C	0.500 hour @Temperature 73.4 °F	Zinc, handling strength
	30.0 min @Temperature 23.0 °C	0.500 hour @Temperature 73.4 °F	M10 steel, working strength
	180 min @Temperature 23.0 °C	3.00 hour @Temperature 73.4 °F	Stainless steel, handling strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	Zinc, working strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	M10 steel, full strength

Descriptive Properties	Value	Comments
Appearance	Blue	Uncured
Maximum Gap Fill (mm)	0.12
Maximum Thread Size	M20
Strength Retention	20% at 150°C	Relative to 0°C
	70% at 100°C	Relative to 0°C
	90% at 50°C	Relative to 0°C
Torque Strength (N m)	16	M10 steel, break
	8	M10 steel, prevail
UV Fluorescence	Yes	Uncured