PTS Trimid® N66-T100 Toughened Nylon 6/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N66-T100 Toughened Nylon 6/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 75 % | 75 % | ASTM D638 |
| Flexural Modulus | 1.72 GPa | 249 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 252 °C | 486 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 1500L (C30G) Propylene Homopolymer
- RheTech Products HP513-00A High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- PolyOne Edgetek® SF-35GF-25MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
- Hong Kun Group UV Absorber
- Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 25 µm)
- Indium Corp. NanoFoil® NF40 Nickel and Aluminum Localized Heat Source For Bonding
- Techmer ES Luriblend® PEI CF30 TL15 30% Carbon Filled
- Teknor Apex APEX® 90-A472R-60-NT Polyvinyl Chloride, Flexible
- Total HDPE 46060 UV High Density Polyethylene - Large Part Blow Molding Resin
- Abatron AboCast/AboCure 8109-10
Copyright © lookpolymers.com All Rights Reserved