- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- PTS Trilac® ABS-HS7500 High Impact ABS Resin
PTS Trilac® ABS-HS7500 High Impact ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-HS7500 High Impact ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
| Flexural Yield Strength | 63.4 MPa | 9200 psi | ASTM D790 |
| Flexural Modulus | 2.15 GPa | 312 ksi | ASTM D790 |
| Izod Impact, Notched | 3.31 J/cm @Thickness 6.35 mm |
6.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.00 J/cm @Thickness 3.17 mm |
7.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 92 % | 92 % | Gardner Gloss @ 60° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 2040 Liquid Silicone Rubber - General Purpose
- Styrolution Luran® 378 P Crystal Clear Transparent SAN
- Terio Corporation TCZA-20~80 CeO2-Al2O3-ZrO2
- Cytec Thornel® T-300 1K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy
- Arlon Thermabond® 99950N015 Silicone Rubber/Fiberglass Laminate
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.5 PHR Thanecure ZM
- 3M Dyneon™ CC132 Custom Fluoropolymer Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved