SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.246 g/cc | 0.04501 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.810 % | 0.810 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | 5 mm/min; ISO 527 |
| 173 MPa | 25100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.96 GPa | 1440 ksi | 1 mm/min; ISO 527 |
| 10.5 GPa | 1520 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| 241 MPa | 35000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.92 GPa | 1150 ksi | 2 mm/min; ISO 178 |
| 8.26 GPa | 1200 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.14 J/cm | 9.63 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.49 | 0.49 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D3702 Modified |
| K (wear) Factor | 72.5 x 10-8 mm³/N-M | 36.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
42.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 787K (RL) Synthetic Oil
- Precision Polymer Engineering N90L Nitrile Rubber
- Precision Polymer Engineering R70Z Natural Rubber
- Northstar Polymers BNA-005 Polyester Curing Agent
- PTS Trimid® N6-G30L 30% GFR Lubricated Nylon 6
- Latrobe BG42® Stainless Knife Steel (AMS 5749)
- SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12
- Williams Advanced Alloys WS221 Solder
- Polyram PlusTek PB145 Nylon 6, Injection Molding
- Ashley Polymers Ashlene® ABS Resin E213B
Copyright © lookpolymers.com All Rights Reserved