PTS PCA-FR Eco-Friendly, High Flow, Flame Retardant PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PCA-FR Eco-Friendly, High Flow, Flame Retardant PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a non-halogenated flame retardant grade. Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 16 g/10 min @Load 2.20 kg, Temperature 260 °C |
16 g/10 min @Load 4.85 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa @Thickness 3.17 mm |
8990 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 40 % @Thickness 3.17 mm |
40 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 96.0 MPa @Thickness 3.17 mm |
13900 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.57 GPa @Thickness 3.17 mm |
373 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 266 °C | 450 - 510 °F | |
| Middle Barrel Temperature | 246 - 274 °C | 475 - 525 °F | |
| Front Barrel Temperature | 246 - 288 °C | 475 - 550 °F | |
| Nozzle Temperature | 246 - 288 °C | 475 - 550 °F | |
| Melt Temperature | 246 - 288 °C | 475 - 550 °F | |
| Mold Temperature | 57.2 - 85.0 °C | 135 - 185 °F | |
| Drying Temperature | 96.1 °C | 205 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.9 - 110 MPa | 10000 - 16000 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Screw Speed | 25 - 75 rpm | 25 - 75 rpm |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5701 Black PP
- Lehmann & Voss LUVOCOM® 1105-8169 PEEK, with carbon fiber
- Lehmann & Voss LUVOCOM® 1-8357 Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- KKPC KOSYN KSL 208 Styrene-Butadiene Latex
- Multibase Multi-Flex® A 9002 MR TPE Thermoplastic Elastomer
- Sharadaa Ceramics REFCAST LC60 Low Cement Castables
- Zircar Zirconia ZYBF-5 Zirconia Bulk Fiber Insulation
- Tra-Con Tra-Cast 3109 Low Cost Epoxy Casting System
- Pyrotek Pyrocast SC-2600 Refractory Cast Parts
- LG Chemical LI923 Extrusion ASA
Copyright © lookpolymers.com All Rights Reserved