Oxford Polymers ABS 20CCF-MP-BK ABS, 20% Carbon Fiber Reinforced

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Carbon Fiber Filled
Manufacturer	Oxford Polymers
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Oxford Polymers ABS 20CCF-MP-BK ABS, 20% Carbon Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Conductive Carbon Fiber (20% Reinforced), ABS injection molding grade Processing and Delivery Form: Pellets and extrusion/Injection Molding Additives: Release AgentsInformation provided by Oxford Polymers

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ASTM D792
Ash	20.0 %	20.0 %	ASTM 5630B

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	ASTM D638
Elongation at Break	2.00 %	2.00 %	ASTM D638
Flexural Strength	131 MPa	19000 psi	ASTM D790
Flexural Modulus	10.0 GPa	1450 ksi	ASTM D790
Izod Impact, Notched	0.694 J/cm @Thickness 3.17 mm	1.30 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	87.8 °C	190 °F	ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 100 ohm-cm	<= 100 ohm-cm	conductive

Processing Properties	Metric	English
Rear Barrel Temperature	188 - 210 °C	370 - 410 °F
Middle Barrel Temperature	204 - 227 °C	400 - 440 °F
Front Barrel Temperature	216 - 238 °C	420 - 460 °F
Nozzle Temperature	218 - 260 °C	425 - 500 °F
Melt Temperature	218 - 249 °C	425 - 480 °F
Mold Temperature	48.9 - 71.1 °C	120 - 160 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	2.00 hour	2.00 hour