Arlon 28941C015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 28941C015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene Interleave |
| >= 88.9 microns | >= 3.50 mil | Side 1 | |
| >= 88.9 microns | >= 3.50 mil | Side 2 | |
| 203 microns | 8.00 mil | Prime Coated 1528 Fiberglass, Substrate | |
| 330 - 432 microns | 13.0 - 17.0 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 - 60 | 50 - 60 | Compound Property |
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Elongation at Break | >= 450 % | >= 450 % | Compound Property |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | V-0 | V-0 | per card E54153 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 177 °C |
0.250 hour @Temperature 350 °F |
Recommended Cure Cycle |
| 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Brown | |
| Total Product Weight (oz/yd2) | 15.3 - 18.3 | |
| Uncoated Fabric Break Strength | 180 lb/in | Fill Direction, Substrate Property |
| 225 lb/in | Warp Direction, Substrate Property |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 940ASR PC (Asia Pacific)
- Lehmann & Voss LUVOCOM® 19-8074 Polyamide 46, with aramid reinforcement and PTFE
- LG Chemical LUMID HI1102A(W) PA6, High Impact
- Michelman® DigiGuard® Gloss 100 Water based overprint varnish
- Solvay TECHNYL® A 218 V40 Black 21 NHFE PA66, 40% glass fiber, DRY
- Westlake EMAC® SP2404 18.5% EMA Copolymer
- Fainplast Compounds RE 121 Rigid PVC, Extrusion
- Arlon 30570XA015 0.015" (0.381mm) Uncured/Unsupported Silicone Rubber on a Release Carrier
- Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable
Copyright © lookpolymers.com All Rights Reserved