Overview of materials for Nylon 66, 20% Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 20% Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.14 - 1.50 g/cc
0.0412 - 0.0542 lb/in³
Average value: 1.24 g/cc Grade Count:33
Filler Content 15.0 - 20.0 %
15.0 - 20.0 %
Average value: 18.0 % Grade Count:10
Water Absorption 0.400 - 2.50 %
0.400 - 2.50 %
Average value: 0.853 % Grade Count:17
Moisture Absorption at Equilibrium 0.400 - 2.50 %
0.400 - 2.50 %
Average value: 1.86 % Grade Count:5
Water Absorption at Saturation 5.00 - 8.00 %
5.00 - 8.00 %
Average value: 6.20 % Grade Count:5
Additive Loading 15.0 - 20.0 %
15.0 - 20.0 %
Average value: 18.3 % Grade Count:3
Linear Mold Shrinkage 0.000500 - 0.0180 cm/cm
0.000500 - 0.0180 in/in
Average value: 0.00327 cm/cm Grade Count:31
Linear Mold Shrinkage, Transverse 0.00190 - 0.0110 cm/cm
0.00190 - 0.0110 in/in
Average value: 0.00698 cm/cm Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114 - 125
114 - 125
Average value: 119 Grade Count:12
Ball Indentation Hardness 160 - 270 MPa
23200 - 39200 psi
Average value: 223 MPa Grade Count:3
Tensile Strength, Ultimate 125 - 230 MPa
18100 - 33400 psi
Average value: 182 MPa Grade Count:27
90.0 - 140 MPa

@Temperature 60.0 - 150 °C
13100 - 20300 psi

@Temperature 140 - 302 °F
Average value: 113 MPa Grade Count:1
Tensile Strength, Yield 152 - 230 MPa
22000 - 33400 psi
Average value: 183 MPa Grade Count:6
Elongation at Break 1.00 - 5.00 %
1.00 - 5.00 %
Average value: 2.79 % Grade Count:33
2.70 - 3.70 %

@Temperature 60.0 - 150 °C
2.70 - 3.70 %

@Temperature 140 - 302 °F
Average value: 3.35 % Grade Count:1
Modulus of Elasticity 9.00 - 18.6 GPa
1310 - 2700 ksi
Average value: 14.0 GPa Grade Count:26
5.40 - 14.0 GPa

@Temperature 60.0 - 150 °C
783 - 2030 ksi

@Temperature 140 - 302 °F
Average value: 9.23 GPa Grade Count:1
Flexural Yield Strength 193 - 330 MPa
28000 - 47900 psi
Average value: 263 MPa Grade Count:26
Flexural Modulus 6.55 - 16.2 GPa
950 - 2350 ksi
Average value: 12.3 GPa Grade Count:28
Compressive Yield Strength 131 - 172 MPa
19000 - 25000 psi
Average value: 145 MPa Grade Count:3
Izod Impact, Notched 0.534 - 1.92 J/cm
1.00 - 3.60 ft-lb/in
Average value: 0.871 J/cm Grade Count:22
Izod Impact, Unnotched 5.34 - 9.08 J/cm
10.0 - 17.0 ft-lb/in
Average value: 6.80 J/cm Grade Count:14
Izod Impact, Notched (ISO) 5.00 - 8.00 kJ/m²
2.38 - 3.81 ft-lb/in²
Average value: 7.00 kJ/m² Grade Count:3
3.00 - 6.00 kJ/m²

@Temperature -40.0 - -20.0 °C
1.43 - 2.86 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 4.50 kJ/m² Grade Count:2
Charpy Impact Unnotched 2.60 - 7.20 J/cm²
12.4 - 34.3 ft-lb/in²
Average value: 4.53 J/cm² Grade Count:8
2.50 - 4.10 J/cm²

@Temperature -40.0 - -20.0 °C
11.9 - 19.5 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.03 J/cm² Grade Count:3
Charpy Impact, Notched 0.600 - 1.60 J/cm²
2.86 - 7.61 ft-lb/in²
Average value: 0.872 J/cm² Grade Count:8
0.400 - 0.500 J/cm²

@Temperature -40.0 - -20.0 °C
1.90 - 2.38 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 0.450 J/cm² Grade Count:2
Thermal Properties Metric English Comments
CTE, linear 17.0 - 68.4 µm/m-°C
9.44 - 38.0 µin/in-°F
Average value: 34.6 µm/m-°C Grade Count:15
Melting Point 221 - 262 °C
430 - 504 °F
Average value: 253 °C Grade Count:9
Maximum Service Temperature, Air 115 - 240 °C
239 - 464 °F
Average value: 155 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 240 - 260 °C
464 - 500 °F
Average value: 253 °C Grade Count:15
Deflection Temperature at 1.8 MPa (264 psi) 230 - 259 °C
446 - 498 °F
Average value: 248 °C Grade Count:28
Vicat Softening Point 230 - 255 °C
446 - 491 °F
Average value: 248 °C Grade Count:5
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:24
Electrical Properties Metric English Comments
Electrical Resistivity 10.0 - 1.00e+7 ohm-cm
10.0 - 1.00e+7 ohm-cm
Average value: 878000 ohm-cm Grade Count:26
Surface Resistance 20.0 - 1.00e+7 ohm
20.0 - 1.00e+7 ohm
Average value: 1.11e+6 ohm Grade Count:13
Processing Properties Metric English Comments
Processing Temperature 270 - 300 °C
518 - 572 °F
Average value: 284 °C Grade Count:7
Melt Temperature 260 - 300 °C
500 - 572 °F
Average value: 283 °C Grade Count:14
Mold Temperature 60.0 - 110 °C
140 - 230 °F
Average value: 85.7 °C Grade Count:21
Drying Temperature 75.0 - 100 °C
167 - 212 °F
Average value: 81.0 °C Grade Count:13
Moisture Content 0.150 - 0.200 %
0.150 - 0.200 %
Average value: 0.195 % Grade Count:11
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:7
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 102 MPa Grade Count:14