PolyOne Therma-Tech™ NJC-7500 TC Nylon 12  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Therma-Tech™ NJC-7500 TC Nylon 12  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications.Description/Features:PA 12 (Nylon 12)Thermally ConductiveElectrically ConductiveApplications: EnclosuresHeat SinksMotor componentsProcessing Method: Injection MoldingInformation provided by PolyOne Corporation
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D792
Water Absorption 0.10 %

@Thickness 3.17 mm
0.10 %

@Thickness 0.125 in
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 39.3 MPa
5700 psi
Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
Elongation at Break 0.40 %
0.40 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 14.5 GPa
2100 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 11.415 GPa
1655.6 ksi
ASTM D790
Izod Impact, Notched 0.160 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
0.300 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 20.0 - 24.9 W/m-K
139 - 173 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
380 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm - 1e+05
10000 ohm-cm - 1e+05
ASTM D257
Surface Resistivity per Square 1000 - 30000 ohm
1000 - 30000 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 260 - 277 °C
500 - 530 °F
Molding
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F