Polymer Property : Tensile Strength, Ultimate = 5510 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	38.0 MPa @Temperature 90.0 °C	5510 psi @Temperature 194 °F	ISO 527
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
PolyOne Lubri-Tech™ AT-15GP/05T Acetal With Graphite - 5% PTFE (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	38.0 - 85.0 MPa @Temperature 60.0 - 120 °C	5510 - 12300 psi @Temperature 140 - 248 °F	Average value: 58.4 MPa Grade Count:3
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
Global GM-2860 High Density Polyethylene, Injection Molding Grade (discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesMeets FDA requirements as listed in..
Tensile Strength, Ultimate	38.0 - 150 MPa	5510 - 21800 psi	Average value: 78.2 MPa Grade Count:87
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate	38.0 - 110 MPa	5510 - 16000 psi	Average value: 88.2 MPa Grade Count:25
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..
Tensile Strength, Ultimate	38.0 MPa	5510 psi
Haveg 41NA Phenolic; Silicate Filled A proprietary thermoset plastic consisting of a phenol-formaldehyde resin and non-asbestos silicate fillers.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa @Temperature -20.0 °C	5510 psi @Temperature -4.00 °F	Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638
DuPont Elvax® 670 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	at max load; ISO 527
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ISO 527-1, 2
Polyplastics Duracon® SF-15 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Tensile Strength, Ultimate	38.0 MPa @Temperature 80.0 °C	5510 psi @Temperature 176 °F	ASTM D638
Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	DIN 53504
Lubrizol ESTANE® 5778 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ISO 527-1
Chengdu Polyster CH7563 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with PBT, PET and PA. For blending with PBT, PET and PA to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638/D412
Covestro Bayflex® 190 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System 0.150 in. thickness. Calcium Silicate filled. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was se..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	cond; ISO 527-1/-2
DSM Novamid® 1010GN7-20 BK37 PA6-GF20 FR(30) 0 20% Glass Reinforced, Flame Retardant, Halogen free
Tensile Strength, Ultimate	38.0 - 47.0 MPa	5510 - 6820 psi
Arkema Group Rilsan® Fine Powders Grey 49 Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p..
Tensile Strength, Ultimate	38.0 - 47.0 MPa	5510 - 6820 psi
Arkema Group Rilsan® Fine Powders Natural Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p..
Tensile Strength, Ultimate	38.0 - 47.0 MPa	5510 - 6820 psi
Arkema Group Rilsan® Fine Powders Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
Solvay Specialty Polymers Algoflon® 0.1 Mos PTFE; Molybdenum Disulfide Filled (discontinued **) Data provided by the manufacturer.0.1 wt.% Molybdenum Disulfide. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric propert..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	38.0 MPa	5510 psi	DIN 53504
Lubrizol ESTANE® T5191 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
Plenco 7321 Phenolic, Nodular, Compression Molded PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon..
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ASTM D638
Sumitomo Bakelite North America FM 3000 Cellulose Reinforced Phenolic Novolac FM 3000 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. Information supplied by Sumitomo Bak North America...
Tensile Strength, Ultimate	38.0 MPa	5510 psi	ISO 527-1, 2
Polyplastics Duracon® TD-20 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..