Overview of materials for Nylon 11 with 20% Glass Fiber Filler

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 20% Glass Fiber Filler
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Nylon 11 with 20% Glass Fiber Filler.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.13 - 1.50 g/cc	0.0408 - 0.0542 lb/in³	Average value: 1.30 g/cc Grade Count:12
Filler Content	15.0 - 20.0 %	15.0 - 20.0 %	Average value: 18.0 % Grade Count:5
Water Absorption	0.160 - 1.20 %	0.160 - 1.20 %	Average value: 0.388 % Grade Count:5
Additive Loading	15.0 - 20.0 %	15.0 - 20.0 %	Average value: 18.0 % Grade Count:5
Linear Mold Shrinkage	0.00200 - 0.00600 cm/cm	0.00200 - 0.00600 in/in	Average value: 0.00400 cm/cm Grade Count:10

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	108 - 109	108 - 109	Average value: 108 Grade Count:4
Tensile Strength, Ultimate	68.9 - 110 MPa	10000 - 16000 psi	Average value: 81.7 MPa Grade Count:12
Elongation at Break	2.00 - 5.00 %	2.00 - 5.00 %	Average value: 3.42 % Grade Count:12
Modulus of Elasticity	3.79 - 7.69 GPa	550 - 1120 ksi	Average value: 5.39 GPa Grade Count:12
Flexural Yield Strength	96.5 - 117 MPa	14000 - 17000 psi	Average value: 107 MPa Grade Count:10
Flexural Modulus	3.03 - 5.52 GPa	440 - 800 ksi	Average value: 4.39 GPa Grade Count:10
Izod Impact, Notched	0.534 - 1.07 J/cm	1.00 - 2.00 ft-lb/in	Average value: 0.849 J/cm Grade Count:10
Izod Impact, Unnotched	4.27 - 6.41 J/cm	8.00 - 12.0 ft-lb/in	Average value: 5.29 J/cm Grade Count:10
Charpy Impact Unnotched	8.29 - 8.49 J/cm² @Temperature -30.0 - -30.0 °C	39.5 - 40.4 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 8.39 J/cm² Grade Count:2
Charpy Impact, Notched	0.940 - 0.990 J/cm² @Temperature -30.0 - -30.0 °C	4.47 - 4.71 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 0.965 J/cm² Grade Count:2

Thermal Properties	Metric	English	Comments
CTE, linear	50.0 - 72.0 µm/m-°C	27.8 - 40.0 µin/in-°F	Average value: 63.5 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi)	171 - 179 °C	340 - 355 °F	Average value: 177 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi)	163 - 174 °C	325 - 345 °F	Average value: 169 °C Grade Count:6
Flammability, UL94	HB - V-0	HB - V-0	Grade Count:12

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+13 - 2.00e+13 ohm-cm	1.00e+13 - 2.00e+13 ohm-cm	Average value: 1.20e+13 ohm-cm Grade Count:5
Dielectric Strength	19.7 - 22.0 kV/mm	500 - 559 kV/in	Average value: 20.5 kV/mm Grade Count:3
Dissipation Factor	0.000460 - 0.0150	0.000460 - 0.0150	Average value: 0.00649 Grade Count:3

Processing Properties	Metric	English	Comments
Processing Temperature	216 - 282 °C	420 - 540 °F	Average value: 249 °C Grade Count:5
Melt Temperature	224 - 288 °C	435 - 550 °F	Average value: 256 °C Grade Count:5
Mold Temperature	37.8 - 65.6 °C	100 - 150 °F	Average value: 51.7 °C Grade Count:10
Drying Temperature	79.4 °C	175 °F	Average value: 79.4 °C Grade Count:5
Moisture Content	0.200 %	0.200 %	Average value: 0.200 % Grade Count:5
Dew Point	-17.8 °C	0.000 °F	Average value: -17.8 °C Grade Count:5
Injection Pressure	68.9 - 103 MPa	10000 - 15000 psi	Average value: 86.2 MPa Grade Count:10