Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.07 - 1.40 g/cc
0.0387 - 0.0506 lb/in³
Average value: 1.14 g/cc Grade Count:60
Filler Content 5.00 - 15.0 %
5.00 - 15.0 %
Average value: 9.79 % Grade Count:14
Water Absorption 0.100 - 0.300 %
0.100 - 0.300 %
Average value: 0.224 % Grade Count:22
Maximum Moisture Content 0.0200 - 0.150
0.0200 - 0.150
Average value: 0.0525 Grade Count:4
Linear Mold Shrinkage 0.00100 - 0.00900 cm/cm
0.00100 - 0.00900 in/in
Average value: 0.00321 cm/cm Grade Count:56
Linear Mold Shrinkage, Transverse 0.00200 - 0.00400 cm/cm
0.00200 - 0.00400 in/in
Average value: 0.00283 cm/cm Grade Count:3
Melt Flow 0.100 - 42.0 g/10 min
0.100 - 42.0 g/10 min
Average value: 7.62 g/10 min Grade Count:26
Ash 9.70 - 10.0 %
9.70 - 10.0 %
Average value: 9.93 % Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 55.0 - 102
55.0 - 102
Average value: 73.4 Grade Count:5
Hardness, Rockwell R 55.0 - 115
55.0 - 115
Average value: 104 Grade Count:19
Tensile Strength, Ultimate 26.0 - 98.1 MPa
3770 - 14200 psi
Average value: 58.0 MPa Grade Count:34
28.0 - 46.0 MPa

@Temperature 60.0 - 90.0 °C
4060 - 6670 psi

@Temperature 140 - 194 °F
Average value: 37.0 MPa Grade Count:1
Tensile Strength, Yield 28.0 - 88.3 MPa
4060 - 12800 psi
Average value: 59.4 MPa Grade Count:38
Elongation at Break 2.00 - 10.0 %
2.00 - 10.0 %
Average value: 3.85 % Grade Count:43
Elongation at Yield 1.90 - 6.00 %
1.90 - 6.00 %
Average value: 3.11 % Grade Count:8
Modulus of Elasticity 2.50 - 5.88 GPa
363 - 853 ksi
Average value: 3.66 GPa Grade Count:21
Flexural Yield Strength 62.1 - 108 MPa
9010 - 15700 psi
Average value: 87.3 MPa Grade Count:52
Flexural Modulus 2.34 - 5.88 GPa
340 - 853 ksi
Average value: 3.72 GPa Grade Count:59
Izod Impact, Notched 0.490 - 1.80 J/cm
0.919 - 3.37 ft-lb/in
Average value: 0.764 J/cm Grade Count:58
0.450 - 1.50 J/cm

@Temperature -40.0 - 0.000 °C
0.843 - 2.81 ft-lb/in

@Temperature -40.0 - 32.0 °F
Average value: 0.579 J/cm Grade Count:2
0.300 - 0.500 J/cm

@Temperature -30.0 - 0.000 °C
0.562 - 0.937 ft-lb/in

@Temperature -22.0 - 32.0 °F
Average value: 0.579 J/cm Grade Count:1
0.300 - 0.500 J/cm

@Thickness 3.20 - 3.20 mm
0.562 - 0.937 ft-lb/in

@Thickness 0.126 - 0.126 in
Average value: 0.579 J/cm Grade Count:1
Izod Impact, Unnotched 2.14 - 3.47 J/cm
4.00 - 6.50 ft-lb/in
Average value: 2.97 J/cm Grade Count:18
Thermal Properties Metric English Comments
CTE, linear 23.0 - 57.6 µm/m-°C
12.8 - 32.0 µin/in-°F
Average value: 43.9 µm/m-°C Grade Count:12
Deflection Temperature at 0.46 MPa (66 psi) 93.3 - 112 °C
200 - 233 °F
Average value: 102 °C Grade Count:29
Deflection Temperature at 1.8 MPa (264 psi) 83.9 - 114 °C
183 - 237 °F
Average value: 97.0 °C Grade Count:49
Vicat Softening Point 96.0 - 111 °C
205 - 232 °F
Average value: 104 °C Grade Count:10
UL RTI, Electrical 50.0 - 60.0 °C
122 - 140 °F
Average value: 56.0 °C Grade Count:3
UL RTI, Mechanical with Impact 50.0 - 60.0 °C
122 - 140 °F
Average value: 56.0 °C Grade Count:3
UL RTI, Mechanical without Impact 50.0 - 60.0 °C
122 - 140 °F
Average value: 56.0 °C Grade Count:3
Flammability, UL94 HB - 5VB
HB - 5VB
Grade Count:33
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+9 - 1.00e+16 ohm-cm
1.00e+9 - 1.00e+16 ohm-cm
Average value: 5.32e+15 ohm-cm Grade Count:16
Surface Resistance 1.00e+10 - 1.00e+14 ohm
1.00e+10 - 1.00e+14 ohm
Average value: 5.00e+13 ohm Grade Count:4
Dielectric Constant 3.00 - 3.30
3.00 - 3.30
Average value: 3.17 Grade Count:3
Dielectric Strength 15.7 - 30.0 kV/mm
400 - 762 kV/in
Average value: 20.1 kV/mm Grade Count:13
Dissipation Factor 0.00800 - 0.0200
0.00800 - 0.0200
Average value: 0.0127 Grade Count:3
Arc Resistance 60.0 - 180 sec
60.0 - 180 sec
Average value: 107 sec Grade Count:3
Comparative Tracking Index 175 - 500 V
175 - 500 V
Average value: 308 V Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 193 - 232 °C
380 - 450 °F
Average value: 214 °C Grade Count:4
Nozzle Temperature 177 - 274 °C
350 - 525 °F
Average value: 230 °C Grade Count:6
Melt Temperature 168 - 274 °C
335 - 525 °F
Average value: 221 °C Grade Count:17
Mold Temperature 40.0 - 93.3 °C
104 - 200 °F
Average value: 67.8 °C Grade Count:21
Drying Temperature 70.0 - 100 °C
158 - 212 °F
Average value: 85.4 °C Grade Count:15
Moisture Content 0.100 %
0.100 %
Average value: 0.100 % Grade Count:5
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:4
Injection Pressure 4.83 - 150 MPa
700 - 21800 psi
Average value: 76.2 MPa Grade Count:12