- Techmer ES Luriblend® PA6/6 CF30 TL15 HS BK 30% Carbon Filled
Techmer ES Luriblend® PA6/6 CF30 TL15 HS BK 30% Carbon Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled , Nylon 66, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 CF30 TL15 HS BK 30% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Heat StabilizerFeatures: Lubricated, Good Wear Resistance, Heat Stabilized and Low Friction Appearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.48 % @Time 86400 sec |
0.48 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 286 MPa | 41500 psi | ASTM D790 |
| Flexural Modulus | 13.7 GPa | 1980 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D1894 |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D1894 |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.771 MPa-m/sec | 22000 psi-ft/min | 1000 fpm |
| 1.05 MPa-m/sec | 30000 psi-ft/min | 10 fpm | |
| 1.54 MPa-m/sec | 44000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 488 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 10000 ohm-cm | 10 - 10000 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 760A (NG) Synthetic Oil
- PolyOne Geon™ Vinyl Flexible B65B0 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kingfa MAC-601 DY Modified 60/40 PC/ABS Alloy
- H.C. Starck Amperit® 512.074 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- Solvay TECHNYL® 2710IR PA66, Conditioned
- A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene
- China Tungsten YW1 Tungsten Carbide for Cutting Tools
- 3M Scotchcal™ ElectroCut™ 7725-197 Graphic Film
- RheTech Products HP506-01B 22% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved