Overview of materials for Acrylic, UV Stabilized, Molded

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, UV Stabilized, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylic, UV Stabilized, Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, UV Stabilized, Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.20 g/cc
0.0415 - 0.0434 lb/in³
Average value: 1.18 g/cc Grade Count:14
Water Absorption 0.300 - 1.90 %
0.300 - 1.90 %
Average value: 0.617 % Grade Count:6
Linear Mold Shrinkage 0.00200 - 0.00800 cm/cm
0.00200 - 0.00800 in/in
Average value: 0.00500 cm/cm Grade Count:8
Melt Flow 1.10 - 26.0 g/10 min
1.10 - 26.0 g/10 min
Average value: 4.90 g/10 min Grade Count:13
Mechanical Properties Metric English Comments
Hardness, Rockwell M 20.0 - 94.0
20.0 - 94.0
Average value: 67.7 Grade Count:7
Tensile Strength, Ultimate 32.4 - 70.3 MPa
4700 - 10200 psi
Average value: 59.1 MPa Grade Count:13
Elongation at Break 2.00 - 50.0 %
2.00 - 50.0 %
Average value: 13.8 % Grade Count:5
Modulus of Elasticity 1.79 - 3.45 GPa
260 - 500 ksi
Average value: 2.77 GPa Grade Count:9
Flexural Yield Strength 55.2 - 117 MPa
8000 - 17000 psi
Average value: 90.3 MPa Grade Count:8
Flexural Modulus 1.72 - 3.45 GPa
250 - 500 ksi
Average value: 2.69 GPa Grade Count:8
Izod Impact, Notched 0.160 - 0.587 J/cm
0.300 - 1.10 ft-lb/in
Average value: 0.322 J/cm Grade Count:8
Thermal Properties Metric English Comments
CTE, linear 72.0 - 72.0 µm/m-°C

@Temperature 0.000 - 156 °C
40.0 - 40.0 µin/in-°F

@Temperature 32.0 - 312 °F
Average value: 72.0 µm/m-°C Grade Count:2
Thermal Conductivity 0.187 - 0.216 W/m-K
1.30 - 1.50 BTU-in/hr-ft²-°F
Average value: 0.205 W/m-K Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 85.0 - 105 °C
185 - 221 °F
Average value: 95.4 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 73.9 - 102 °C
165 - 216 °F
Average value: 89.7 °C Grade Count:14
Vicat Softening Point 76.7 - 114 °C
170 - 237 °F
Average value: 100 °C Grade Count:13
Optical Properties Metric English Comments
Refractive Index 1.49
1.49
Average value: 1.49 Grade Count:5
Haze 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 2.25 % Grade Count:12
Transmission, Visible 80.0 - 92.0 %
80.0 - 92.0 %
Average value: 90.3 % Grade Count:13
Processing Properties Metric English Comments
Mold Temperature 26.7 - 107 °C
80.0 - 225 °F
Average value: 66.0 °C Grade Count:3