Ovation Polymers Nemcon™ H ABS DP116P ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Ovation Polymers |
| Trade Name | Nemcon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ovation Polymers Nemcon™ H ABS DP116P ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS-Thermally conducting, electrically insulating grade with high HDT and improved processability.Information provided by Ovation Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 3.572 GPa | 518.1 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 52.0 MPa | 7540 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.188 GPa | 462.4 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm @Temperature 23.0 °C |
0.401 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | ASTM E-1461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 8.00e+12 ohm | 8.00e+12 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 220 - 270 °C | 428 - 518 °F | |
| Zone 1 | 220 - 255 °C | 428 - 491 °F | |
| Zone 2 | 220 - 260 °C | 428 - 500 °F | |
| Zone 3 | 220 - 265 °C | 428 - 509 °F | |
| Melt Temperature | 220 - 275 °C | 428 - 527 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Back Pressure | 0.207 - 0.552 MPa | 30.0 - 80.0 psi | |
| Screw Speed | 70 - 100 rpm | 70 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific)
- Kotec Carbotex K-30MRA Polycarbonate, General Purpose, Mold Release Grade
- ChevronTexaco SAE 40 Military Symbol 9250 Engine Oil
- Abatron AboCoat 8709-2 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Braskem PB682 Blow Molding Low Density Polyethylene
- 3M Scotch® 77 Black Fire-Retardant Electric Arc Proofing Tape
- E-Polymers EFLEX® S1050 General
- DuPont Performance Polymers Neoprene FB Polychloroprene Rubber (discontinued **)
- Sinotek Materials PMF Board Heat Insulation Material Ceramic Fiber Board, White
Copyright © lookpolymers.com All Rights Reserved