Superior Die Set FORTAL® HR Aluminum Alloy
| Category | Metal , Nonferrous Metal , Aluminum Alloy |
| Manufacturer | Superior Die Set |
| Trade Name | Fortal® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Superior Die Set FORTAL® HR Aluminum Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: FORTAL is a high strength, lightweight, easy to machine alloy, originally developed to be used in the aerospace industry. It can be found whenever a structure is highly solicited and doesn't require a very high ratio of resistance/mass. FORTAL offers machinability, high resistance to corrosion, and leads to increased productivity. FORTAL's modulus of elasticity is one third that of steel, and can absorb three times as much shock and vibration in its elastic phase. FORTAL is solution heat-treated, stabilized, artificially aged and stress relieved by stretching. Application: FORTAL is an ideal material for all types of products and tooling since it is stronger than 1020 steels.Information provided by Superior Die Set.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.77 g/cc | 0.100 lb/in³ | |
| Thickness | 14000 - 92000 microns | 551 - 3620 mil | intermediate sizes also available |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 145 | 145 | |
| 150 | 150 | ||
| Tensile Strength, Ultimate | 540.0 MPa | 78320 psi | |
| Tensile Strength, Yield | 480 MPa | 69600 psi | |
| Elongation at Break | 10 % | 10 % | |
| Modulus of Elasticity | 71.98 GPa | 10440 ksi | |
| Fatigue Strength | 80.0 MPa @# of Cycles 1.00e+8 |
11600 psi @# of Cycles 1.00e+8 |
test bar (22mm diam.) notched (Kt = 3) |
| 160 MPa @# of Cycles 1.00e+8 |
23200 psi @# of Cycles 1.00e+8 |
test bar (22mm diam.) unnotched (Kt =1) | |
| Shear Strength | 331 MPa | 48000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.49 µm/m-°C @Temperature 20.0 - 100 °C |
13.05 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.958 J/g-°C | 0.229 BTU/lb-°F | |
| Thermal Conductivity | 130 W/m-K | 902 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 60.0 °C | 140 °F | Recommended |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 90.07 % | 90.07 % | |
| Chromium, Cr | 0.23 % | 0.23 % | |
| Copper, Cu | 1.6 % | 1.6 % | |
| Magnesium, Mg | 2.5 % | 2.5 % | |
| Zinc, Zn | 5.6 % | 5.6 % |
Users viewing this material also viewed the following:
- Permabond LM113 Anaerobic Threadlocker
- PolyOne Geon™ Vinyl Flexible 90215 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Indium Corp. Indalloy 91 Indium Solder Alloy
- LyondellBasell Astryn 65F5-2 Polypropylene Homopolymer, 20% Calcium Carbonate
- SABIC Innovative Plastics LNP THERMOCOMP DZ004 PC
- DuPont Teijin Films Mylar® EB11 Polyester Film, 92 Gauge
- Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded
- CENTROPLAST CENTROMID 6.6 FG Polyamide 6.6, Food Grade
- Total Lacqrene® 6631 Impact Polystyrene (discontinued **)
- LTL Color Compounds ColorFast® FRPC400 Polycarbonate, Flame-Retarded
Copyright © lookpolymers.com All Rights Reserved