Nilit FRIANYL C73 GV40 Nylon 6.6/6 for injection molding, 40% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL C73 GV40 Nylon 6.6/6 for injection molding, 40% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 - 1.7 % | 0.70 - 1.7 % | ISO 62 |
| Water Absorption at Saturation | 4.0 - 5.0 % | 4.0 - 5.0 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0030 - 0.0090 cm/cm | 0.0030 - 0.0090 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 185 MPa | 26800 psi | ISO 2039-1 |
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 |
| 3.20 J/cm² @Temperature -40.0 °C |
15.2 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Proto3000 ABS-M30i Fused Deposition Modeling Polymer
- DSM Akulon® K224-G8U (Dry) 43% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Ineos Nova T263B Expandable Polystyrene
- Wanhua Chemical Wanthane® WHT-7180 Polycaprolactone Based TPU
- Zeon Chemicals Zealloy® 1422 Modifier for Thermoplastics
- Dow Corning 5562 Carbinol Fluid
- Asahi Kasei Thermylene® P-10TC-1777 10% Talc Filled, UV Stabilized Polypropylene
- A. Schulman ComAlloy Hiloy® 221 ABS, Glass Reinforced, UL
- 3M Scotch-Weld™ 2290 Epoxy Adhesive/Coating
- Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled
Copyright © lookpolymers.com All Rights Reserved