- Nilit FRIANYL B63 V0 Nylon 6.6 for injection molding
Nilit FRIANYL B63 V0 Nylon 6.6 for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 V0 Nylon 6.6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, flame retardant, free of halogen and phosphorus.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.012 - 0.025 cm/cm | 0.012 - 0.025 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 135 MPa | 19600 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 2.00 J/cm² @Temperature -40.0 °C |
9.52 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
| 600 V | 600 V | CTI-M 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion L7007 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Qualchem Danamid AFCF-30 Polyamide 66, 30% Carbon Fiber
- KYDEX® 331/331d Co-Extruded High Impact Fire Rated Thermoplastic Sheet with Weatherable Acrylic Film Cap
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 30 lb
- Techmer ES Elastoblend® PA6/6 IM1 HS BK 33% Glass Filled
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- American Elements Titanium Carbide Nanoparticles
- Lubrizol ESTANE® 58562 Ester Based Thermoplastic Polyurethane (European Grade)
- ExxonMobil Bicor® 420 HS OPP Film
Copyright © lookpolymers.com All Rights Reserved