ExxonMobil Exceed™ 3518CB Metallocene Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Exxon Chemical
Trade Name Exceed™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 3518CB Metallocene Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Exceed 3518CB is a metallocene ethylene-hexene copolymer. Films made of Exceed 3518CB grade have outstanding tensile, impact and puncture resistance properties. Furthermore, they are fully stabilized for cast mono and multi layer film production.Availability: Africa & Middle East, Asia Pacific and EuropeAdditive:Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications:Bag in a BoxBarrier Food PackagingBlown Film Cast FilmCast Stretch FilmDiaper BacksheetFood packagingForm Fill and Seal PackagingHygiene FilmPackaging FilmsPersonal Care Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Elmendorf Tear Strength MD 160 g
160 g
ASTM D1922
Elmendorf Tear Strength TD 460 g
460 g
ASTM D1922
Dart Drop Test 180 g
0.397 lb
ASTM D1709
Film Tensile Strength at Break, MD 89.6 MPa
13000 psi
ASTM D882
Film Tensile Strength at Break, TD 55.2 MPa
8000 psi
ASTM D882
1% Secant Modulus, MD 110 MPa
16000 psi
ASTM D882
1% Secant Modulus, TD 131 MPa
19000 psi
ASTM D882
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ASTM D1003
Gloss 14 %
14 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 20 lbf
ExxonMobil Method