Nilit FRIANYL B63 KV15 Nylon 6 for injection molding, 15% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 KV15 Nylon 6 for injection molding, 15% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Water Absorption | 1.7 - 2.7 % | 1.7 - 2.7 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.019 cm/cm | 0.010 - 0.019 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 4.00 J/cm² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® MDX4-4210 Dow-Corning Biomedical Grade Elastomer
- Michelman® Licomer® M 36 Styrene-Acrylate copolymer dispersion
- SSAB Tunnplat Domex® 390YP Cold-forming Steel, HSLA
- SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East)
- STAR Thermoplastic Alloys & Rubbers StarMediflex P 7095-1000 TPE
- Struktol STRUKSILON 8007 Silicone Stabilizer for PU-Rigid Foam
- Saint-Gobain Meldin® 5001 Thermoplastic Bearing Material
- Ter Hell Plastic Terez® PA 6 7450 T GK 30 Polyamide 6, 30% Glass Fiber
- Covestro Makrolon® 2256 Polycarbonate
- Multibase Multibatch® MP 53857 Sheet Extrusion
Copyright © lookpolymers.com All Rights Reserved