- A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 3.0 - 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 23 % | 23 % | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.892 GPa | 419.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.29 J/cm | 9.91 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| DSC Induction Temperature | 165 °C | 329 °F | at 10aC/min; ASTM D3418 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | SE | FMVSS 302 |
| Surface Resistivity | 89 | R-Scale (ASTM D785) |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NH9410 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Europe-Africa-Middle East)
- Eastman 1810E Polyethylene (discontinued **)
- Materion Beryllium Copper Alloy 25 Rod and Bar; H (TD04) Temper; up to 9.5 mm (UNS C17200)
- SABIC Innovative Plastics LNP STAT-KON DD0009 PC
- Styron DL 380 Carboxylated SB
- Borealis Visico™ LE4423/LE4432 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Installation
- ExxonMobil Santoprene® 8221-65M300 Thermoplastic Vulcanizate - UV Resistant
- A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved