Nilit FRIANYL B63 KG30 Nylon 6 for injection molding, 30% chalk filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 KG30 Nylon 6 for injection molding, 30% chalk filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.018 cm/cm | 0.0080 - 0.018 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polykemi AB SCANLON A 5005 PA/ABS-Blend
- MarkeTech Mo60Cu Moly/Copper Heat Sink Material
- LyondellBasell Lupolen® 1810 D LDPE
- Solvay BRICORR® 75 TETRAKIS(HYDROXYMETHYL)PHOSPHONIUM SULPHATE (THPS)
- Solvay Specialty Polymers Halar® 901 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry)
- ExxonMobil NTX™ NTX 150 Super Strength Film Resin
- BASF Ultradur® B 4040 G10 50% Glass Filled BK 15029 PBT + PET
- Addcomp ADD-VANCE® BA 131 Blowing agent
- Hexcel® HexForce™ 7500 Fiber Glass Fabric
Copyright © lookpolymers.com All Rights Reserved