LG Chemical LUPOL EI5002 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL EI5002 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP, General PurposeApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.016 - 0.018 cm/cm @Thickness 3.20 mm |
0.016 - 0.018 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.5 MPa @Thickness 3.20 mm |
3700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 30.4 MPa @Thickness 6.40 mm |
4410 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Flexural Modulus | 1.18 GPa @Thickness 6.40 mm |
171 ksi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.539 J/cm @Thickness 6.40 mm, Temperature -10.0 °C |
>= 1.01 ft-lb/in @Thickness 0.252 in, Temperature 14.0 °F |
ASTM D256 |
| >= 3.92 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 7.35 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- ND Industries NutGrade® 122 Removable Threadlocker
- Invista 3301 PET Copolymer Packaging Resin (discontinued **)
- Parker Chomerics CHO-BOND 1085 Conductive Adhesive
- LG Chemical LUPOL HF5157 PP+Rubber+MF, High Flow and Stiffness, High Impact
- Teknor Apex Terraloy™ BP 13000A Thermoplastic Starch + PP
- DuPont Performance Polymers Sorona® 3015G BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
- ATI Wah Chang Jet Milled Zirconium Oxide, ZrO2
- A. Schulman ComAlloy E-13370B Internally Lubricated, Glass Fiber Reinforced Polyester Alloy
- Abatron AboCast 8103-20 High-Performance Dielectric Epoxy
- BASF Adipic Acid
Copyright © lookpolymers.com All Rights Reserved