Nilit FRIANYL A63 KF30 M2 Nylon 6.6 for injection molding, 30% short glass fiber reinforced and 2% molybdenum disulphide lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 KF30 M2 Nylon 6.6 for injection molding, 30% short glass fiber reinforced and 2% molybdenum disulphide lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.016 cm/cm | 0.0050 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 176 MPa | 25500 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | DIN 53453 |
| 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 592 Conductive Epoxy
- SABIC Innovative Plastics Lexan® 121SRM PC (Asia Pacific)
- Garlock 2102 C.I. SBR/NBR Sheet Rubber, Polyester Insert
- Michelman® Licomer® R 20 Ammonia solution of a rosin, modified with maleic acid
- SCG Chemicals EL-Leneâ„¢ H511W High Density Polyethylene Wire & Cable Grade
- Toho Tenax Besfight® MC Type I (12,000 Filament) Nickel Coated Carbon Fiber
- Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate
- EMS-Grivory Grivory® XE 4174 black 9992 PA1010-GF30
- Victrex® PEEK 450CA20 Polyetheretherketone, 20% Carbon Fibre Reinforced
Copyright © lookpolymers.com All Rights Reserved