- Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced
Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.014 cm/cm | 0.0050 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 |
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527 |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 3.60 J/cm² @Temperature -40.0 °C |
17.1 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | DIN 53453 |
| 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V90M Fluoroelastomer Compound
- MarkeTech Repton 848 Zirconia + 3 mol% Yttria (YSZ)
- MarkeTech WCu15 Tungsten Copper Alloy
- Mitsubishi Iupilon® S2000R 9.5 MFI Polycarbonate With Release
- Isoflon PA 6G Cast Polyamide 6
- ITW Devcon One minuteâ„¢ Epoxy Gel, Amber
- SABIC Innovative Plastics LNP THERMOCOMP EC008PXQ PEI
- Tra-Con Tra-Bond 546S05 Dual-Cure Acrylate
- DSM Arnite® T06 200 (extrusion) PBT (European and Asian Grade)
- Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved