- Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.2 % | 1.5 - 2.2 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.014 cm/cm | 0.0050 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | DIN 53453 |
| 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | |
| 2.80 J/cm² @Temperature -40.0 °C |
13.3 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 3.80 J/cm² @Temperature -30.0 °C |
18.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 | |
| 0.450 J/cm² @Temperature -30.0 °C |
2.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Fujipoly Industries Sarcon® 20GTR Thin-Film GTR
- Misumi G-STAR Martensite Free-cutting Stainless Steel
- SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific)
- EMS-Grivory Grivory® LV-65H FWA black 9225 PA12-GF65
- DuPont™ Nomex® 462 (NOMEX IIIA) Aramid Staple Fiber
- Arlon RBLW401R##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
- 3M Dyneon™ Fluorel™ FLS-2650 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved