- Nilit FRIANYL A63 FK 2010 Nylon 6.6 for injection molding, 20% glass fiber and 10% glass ball reinforced
Nilit FRIANYL A63 FK 2010 Nylon 6.6 for injection molding, 20% glass fiber and 10% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 FK 2010 Nylon 6.6 for injection molding, 20% glass fiber and 10% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.4 % | 1.5 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.013 cm/cm | 0.0050 - 0.013 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 173 MPa | 25100 psi | ISO 2039-1 |
| Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527 |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | DIN 53453 |
| 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU | |
| 2.40 J/cm² @Temperature -40.0 °C |
11.4 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 4.40 J/cm² @Temperature -30.0 °C |
20.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| 0.670 J/cm² | 3.19 ft-lb/in² | ISO 179/1eA | |
| 0.580 J/cm² @Temperature -30.0 °C |
2.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 50 PBT, 50% glass fibre
- LNP Lubricomp® PDX-O-90351 Polyphenylene Sulfide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **)
- Huntsman HY 837 Aliphatic Amine
- Kolon KOCETAL® GF305 G/F Reinforced Acetal Resin
- Silikony Polskie Polimer MV 1.0 Methylvinylsilicone Gum
- Sumitomo Bakelite Durez® 23570 Phenolic, Injection Grade
- Solvay SOPROPHOR® 796/85 Surfactant
- Teknor Apex Telcar® OBC 2318D Thermoplastic Elastomer
- Tra-Con Tra-Bond 216E02 Encapsulant for "Fill" Applications
- China-Yixing Longly Refractories 95 Alumina Ceramic Tubes & Rods
Copyright © lookpolymers.com All Rights Reserved