Nilit FRIANYL A63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.5 - 6.5 % | 5.5 - 6.5 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0070 - 0.015 cm/cm | 0.0070 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 163 MPa | 23600 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.60 J/cm² | 7.61 ft-lb/in² | DIN 53453 |
| 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU | |
| 1.60 J/cm² @Temperature -40.0 °C |
7.61 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| 0.550 J/cm² | 2.62 ft-lb/in² | DIN 53453 | |
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 0.500 J/cm² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 135 °C | 275 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75 |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasadur 3P-H8130B PBT, 30% Glass Fiber Reinforced
- Permabond 791 Cyanoacrylate, Surface insensitive
- Momentive Performance Materials RTV5813 One-Component, Modified Alkoxy Adhesive Sealant, Black
- Solvay Specialty Polymers Amodel® A-4145 HH Polyphthalamide (PPA), 45% Glass Fiber (Dry)
- Techmer ES HiFill® ECTFE GF25 25% Glass Filled
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- Teknor Apex Sinvicomp SIH 5569 Polyvinyl Chloride, Flexible
- BASF Ultrason® E 2010 HC PESU
- 3M Dyneon™ CC085 Custom Fluoropolymer Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved