Multibase Multi-Pro® 2010 M Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 2010 M Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mica Filled, 20% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.3 MPa | 4400 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 216 - 260 °C | 420 - 500 °F | |
| Middle Barrel Temperature | 216 - 260 °C | 420 - 500 °F | |
| Front Barrel Temperature | 221 - 260 °C | 430 - 500 °F | |
| Nozzle Temperature | 216 - 249 °C | 420 - 480 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- PolyOne Elastamax™ XL-2085 Thermoplastic Polyolefin Elastomer (TPO (POE))
- LG Chemical Toluene
- LATI Lastilac AR G/17-V0E ABS, 17% Glass Fiber Reinforced
- Special Metals Nickel 201
- Unitika elitel UE3350 Polyester, Flake
- Polyram PlusTek PB302G50BK39P Nylon 6, 50% Glass Fiber Reinforced, UV and Heat Stabilized
- Wellman Wellamid® T512-BK 15% Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6
- Arlon 48106R008 0.008" (0.203 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- A. Schulman POLYBATCH™ Blue LL40348/4 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved