Mitsubishi Xantar® FC 25 UR Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Mitsubishi
Trade Name Xantar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Xantar® FC 25 UR Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.35 %
0.35 %
Sim. to ISO 62
Viscosity Test 56 cm³/g
56 cm³/g
Limiting Viscosity Number; ISO 1628-4
63 cm³/g
63 cm³/g
Viscosity Number
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ISO 294-4
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
Calculated from Volume Flow Rate of 5 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70
70
ISO 2039-2
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
ISO 527-1/-2
Elongation at Yield 6.0 %
6.0 %
ISO 527-1/-2
Tensile Modulus 2.30 GPa
334 ksi
ISO 527-1/-2
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Izod Impact, Notched (ISO) 80.0 kJ/m²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ISO 180/4A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 20.0 °C
36.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Maximum Service Temperature, Air 125 °C
257 °F
Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
ISO 75-1/-2
Vicat Softening Point 150 °C
302 °F
50°C/h 50N; ISO 306
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL746B
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL746B
UL RTI, Mechanical with Impact 125 °C

@Thickness 1.50 mm
257 °F

@Thickness 0.0591 in
UL746B
125 °C

@Thickness 3.00 mm
257 °F

@Thickness 0.118 in
UL746B
UL RTI, Mechanical without Impact 125 °C

@Thickness 1.50 mm
257 °F

@Thickness 0.0591 in
UL746B
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL746B
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
IEC 60695-11-10
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
IEC 60695-11-20
Oxygen Index 35 %
35 %
ISO 4589-1/-2
Glow Wire Test 825 °C

@Thickness 1.50 mm
1520 °F

@Thickness 0.0591 in
Glow Wire Ignition Temperature; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
IEC 60250
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.00066

@Frequency 100 Hz
0.00066

@Frequency 100 Hz
IEC 60250
0.0092

@Frequency 1e+6 Hz
0.0092

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
Blow Molding Yes
Flame Retardant Yes
Flame Retarding Agent Yes
Heat stabilized or stable to heat Yes
High impact or impact modified Yes
Injection molding Yes
Light stabilized or stable to light Yes
Other Extrusion Yes
Release Agent Yes
U.V. stabilized or stable to weather Yes
Without Fillers Yes