Mitsubishi Xantar® FC 23 UR Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Mitsubishi |
| Trade Name | Xantar® |
| Port | Shanghai port, China |
| Download PDF |
Mitsubishi Xantar® FC 23 UR Polycarbonate.pdf
|
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | Sim. to ISO 62 |
| Viscosity Test | 52 cm³/g | 52 cm³/g | Limiting Viscosity Number; ISO 1628-4 |
| 58 cm³/g | 58 cm³/g | Viscosity Number | |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Melt Flow |
8.4
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
8.4
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 70 | 70 | ISO 2039-2 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-1/-2 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) |
80.0
kJ/m² <br>@Temperature 23.0 °C
|
38.1
ft-lb/in² <br>@Temperature 73.4 °F
|
ISO 180/4A |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow |
65.0
µm/m-°C <br>@Temperature 20.0 °C
|
36.1
µin/in-°F <br>@Temperature 68.0 °F
|
ISO 11359-1/-2 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Ball Pressure Temperature; IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Vicat Softening Point | 148 °C | 298 °F | 50°C/h 50N; ISO 306 |
| UL RTI, Electrical |
130
°C <br>@Thickness 1.50 mm
|
266
°F <br>@Thickness 0.0591 in
|
UL746B |
|
130
°C <br>@Thickness 3.00 mm
|
266
°F <br>@Thickness 0.118 in
|
UL746B | |
| UL RTI, Mechanical with Impact |
125
°C <br>@Thickness 1.50 mm
|
257
°F <br>@Thickness 0.0591 in
|
UL746B |
|
125
°C <br>@Thickness 3.00 mm
|
257
°F <br>@Thickness 0.118 in
|
UL746B | |
| UL RTI, Mechanical without Impact |
125
°C <br>@Thickness 1.50 mm
|
257
°F <br>@Thickness 0.0591 in
|
UL746B |
|
130
°C <br>@Thickness 3.00 mm
|
266
°F <br>@Thickness 0.118 in
|
UL746B | |
| Flammability, UL94 |
V-0
<br>@Thickness 1.60 mm
|
V-0 <br>@Thickness 0.0630 in
|
IEC 60695-11-10 |
|
V-0
<br>@Thickness 3.00 mm
|
V-0 <br>@Thickness 0.118 in
|
IEC 60695-11-10 | |
|
5VA
<br>@Thickness 3.00 mm
|
5VA <br>@Thickness 0.118 in
|
IEC 60695-11-20 | |
| Oxygen Index | 35 % | 35 % | ISO 4589-1/-2 |
| Glow Wire Test |
825
°C <br>@Thickness 1.50 mm
|
1520
°F <br>@Thickness 0.0591 in
|
Glow Wire Ignition Temperature; IEC 60695-2-13 |
|
850
°C <br>@Thickness 3.00 mm
|
1560
°F <br>@Thickness 0.118 in
|
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
|
960
°C <br>@Thickness 1.50 mm
|
1760
°F <br>@Thickness 0.0591 in
|
Glow Wire Flammability Index; IEC 60695-2-12 | |
|
960
°C <br>@Thickness 3.00 mm
|
1760
°F <br>@Thickness 0.118 in
|
Glow Wire Flammability Index; IEC 60695-2-12 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| Blow Molding | Yes | ||
| Flame Retardant | Yes | ||
| Flame Retarding Agent | Yes | ||
| Heat stabilized or stable to heat | Yes | ||
| High impact or impact modified | Yes | ||
| Injection molding | Yes | ||
| Light stabilized or stable to light | Yes | ||
| Release Agent | Yes | ||
| U.V. stabilized or stable to weather | Yes | ||
| Without Fillers | Yes |
| Chemical Resistance Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant |
2.9
<br>@Frequency 1e+6 Hz
|
2.9 <br>@Frequency 1e+6 Hz
|
IEC 60250 |
|
3.0
<br>@Frequency 100 Hz
|
3.0 <br>@Frequency 100 Hz
|
IEC 60250 | |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 |
| Dissipation Factor |
0.00066
<br>@Frequency 100 Hz
|
0.00066 <br>@Frequency 100 Hz
|
IEC 60250 |
|
0.0092
<br>@Frequency 1e+6 Hz
|
0.0092 <br>@Frequency 1e+6 Hz
|
IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| 250 - 399 V | 250 V | PLC 2; UL 746A |
Users viewing this material also viewed:
- PolyOne Geon™ Vinyl Wire & Cable JAC31A Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Maxxam™ DP-8463-7001 Polypropylene Homopolymer (PP Homopolymer)
- ExxonMobil Escorene® LD-319 EVA Film Resin (discontinued **)
- BASF Capron® B85ZP Nylon 6 (DAM) (America) (discontinued **)
- Industrial Laminates/Norplex NP320U Cotton Fabric
- ConocoPhillips Syncon® 10W-30 High Performance Synthetic Motor Oil
- ChevronTexaco 128 Refined Wax
- Dalau Dalcon 021 75% Virgin PTFE, 25% Carbon Coke
- 3M Scotch® 2693 High Performance Masking Tape
Copyright © lookpolymers.com All Rights Reserved