SABIC Innovative Plastics LNP Thermocomp ZZ006 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp ZZ006 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* ZZ006 is a compound based on PPE+PS Blend resin containing Milled Glass.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D 638 |
| 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | Type I, 5 mm/min; ASTM D 638 |
| 4.6 % | 4.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.90 GPa | 711 ksi | 1 mm/min; ISO 527 |
| 5.19 GPa | 753 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 109 MPa | 15800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 4.53 GPa | 657 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 4.71 GPa | 683 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.96 J/cm @Temperature 23.0 °C |
7.42 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 55.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ1028 PC (Europe-Africa-Middle East)
- Honeywell Stretch-Vac® 2000 Heat-Stabilized Blown Film (discontinued **)
- H.C. Starck MoMP 4.5 - 5.5 micron Molybdenum Metal Powder, Mo (99.95%)
- Multibase Multi-Flex® G 7715 TPE Styrene Ethylene Butylene Styrene Block Copolymer
- Teknor Apex APEX® 87-L101F-3 Polyvinyl Chloride, Flexible
- SCG Chemicals EL-Leneâ„¢ S10 Butene (C4) Rotational Molding Resin
- UBE UBEPOL BR360L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- EMS-Grivory Grivory® BG-15/2 PA6-GF15
- BASF Lupranate® 5140 Isocyanate
- BASF Ultramid® A3EG6 30% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved