Mitsubishi Iupilon® S2001R 9.5 MFI FDA Compliant Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Mitsubishi |
| Trade Name | Iupilon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Iupilon® S2001R 9.5 MFI FDA Compliant Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hours at 73°F |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 65 | 65 | ASTM D785 |
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Ultimate | 66.5 MPa @Thickness 3.17 mm |
9650 psi @Thickness 0.125 in |
|
| Tensile Strength, Yield | 60.3 MPa @Thickness 3.17 mm |
8750 psi @Thickness 0.125 in |
|
| Elongation at Break | 120 % @Thickness 3.17 mm |
120 % @Thickness 0.125 in |
|
| Flexural Yield Strength | 87.1 MPa @Thickness 3.17 mm |
12600 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.25 GPa @Thickness 3.17 mm |
326 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 9.45 J/cm @Thickness 3.17 mm |
17.7 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 117 µm/m-°C @Temperature 20.0 °C |
65.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | nD |
| Transmission, Visible | 87 % | 87 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Middle Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Front Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Nozzle Temperature | 277 - 304 °C | 530 - 580 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Clamp Pressure | 27.6 - 68.9 MPa | 4000 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed- Edge Gate | Slow to Medium | |
| Injection Speed- Tab Gate | Medium to Fast | |
| Injection Speed- Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Eastman M2001-P Polyethylene (discontinued **)
- Fine Organics FINALUX G1 Lubricant Additive
- Sylvin Technologies 9925-80 Natural PVC Molding Compound
- Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY
- Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled
- DuPont Teijin Films Melinex® 194 Polyester Film, 380 Gauge
- Aclo Accutech ABS ABS833G40L Glass Reinforced
- 3M Scotch® 8916V Appliance Filament Tape
- Aclo Accutech Polypropylene Copolymer CP0436C20L Calcium Reinforced
- Kolon KOPA® KN3321G15VO G/F Reinforced & Flame Retardant Nylon 66
Copyright © lookpolymers.com All Rights Reserved