Master Bond EP30DPMed USP Class VI, Two Component Epoxy Urethane System

Category Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced , Epoxy, Cast, Unreinforced
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond EP30DPMed USP Class VI, Two Component Epoxy Urethane System.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Master Bond Polymer System EP30DPMED is a versatile, two component, epoxy-urethane elastomeric compound, featuring superior strength, toughness, and abrasion resistance for high performance bonding, sealing, casting and encapsulation. It combines the performance characteristics of epoxy resins such as strength, chemical resistance and adhesive qualities, with those of the polyurethanes including toughness, abrasion resistance and flexibility.
Physical Properties Metric English Comments
Viscosity >= 2500 cP
>= 2500 cP
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
Hardness, Shore D 45
45
Tensile Strength 10.0 MPa
1450 psi
Elongation at Break >= 80 %
>= 80 %
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
Maximum Service Temperature, Air 121 °C
250 °F
Minimum Service Temperature, Air -269 °C
-452 °F
Electrical Properties Metric English Comments
Dielectric Constant 3.8
3.8
Dielectric Strength >= 16.5 kV/mm
>= 420 kV/in
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 93.3 °C
2.00 - 3.00 hour

@Temperature 200 °F
2880 min

@Temperature 23.9 °C
48.0 hour

@Temperature 75.0 °F
Pot Life 2.5 - 3.0 min
2.5 - 3.0 min
100 gram mass
Shelf Life 6.00 Month

@Temperature 23.9 °C
6.00 Month

@Temperature 75.0 °F
in unopened containers
Descriptive Properties Value Comments
Mixing Ratio (A to B) 100/10