Manifattura Cattaneo PVC HI Polyvinyl Chloride
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PVC HI Polyvinyl Chloride.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 - 80 | 78 - 80 | DIN 53505 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.60 | 0.60 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.52 | 0.52 | on polished steel; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 100 °C |
44.4 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 60.0 °C | 140 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
| Vicat Softening Point | 73.0 °C | 163 °F | ISO 306 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Flammability, UL94 | V-1 | V-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60094 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 20.0 - 40.0 kV/mm @Thickness 2.00 mm |
508 - 1020 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Light Gray | |
| UV Resistance | N |
Users viewing this material also viewed the following:
- Spartech SP-9050 Low Gloss ABS Sheet
- SABIC Innovative Plastics LNP Thermocomp RF006XXP PA 66 (Europe-Africa-Middle East)
- ExxonMobil Spartan EP 100
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N774 Filler
- ExxonMobil Label-Lyte® 155 LL-434 Coated, Clear OPP Facestock
- Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer
- Aremco Ceramacast™ 673-N High Temperature Potting & Casting Material Silicon Carbide
- Parker Chomerics CHO-BOND 1073, Part A Silicone Resin Mixture
- PSM Industries PM Krupp 17-4PH Stainless Steel
Copyright © lookpolymers.com All Rights Reserved