- LyondellBasell Hifaxâ„¢ RTA3263/2 Thermoplastic Polyolefin Elastomer
LyondellBasell Hifaxâ„¢ RTA3263/2 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ RTA3263/2 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ RTA3263/2 medium melt flow, 1,700 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good combination of rigidity, impact strength and paintability. It was designed primarily for rigid automotive exterior ornamentation applications. Uses: Automotive exterior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | 0.125 in; ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | ISO 868 & ASTM D2240 |
| Tensile Strength at Break | 17.2 MPa | 2500 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-1, -2 |
| 20.7 MPa | 3000 psi | ASTM D638 | |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1, -2 & ASTM D638 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| 1.72 GPa | 250 ksi | ASTM D790 | |
| Izod Impact, Notched (ISO) | 3.30 kJ/m² @Temperature -40.0 °C |
1.57 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 5.90 kJ/m² @Temperature -30.0 °C |
2.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| 21.0 kJ/m² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Gardner Impact | 14.0 J @Temperature -30.0 °C |
10.3 ft-lb @Temperature -22.0 °F |
ASTM D3029, tested in accordance with ASTM D5420 |
| Dart Drop, Total Energy | 17.0 J @Temperature -30.0 °C |
12.5 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.70 % | 0.70 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 0.900 % @Temperature 121 °C, Time 3600 sec |
0.900 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Ovation Polymers RIGITRON 20415 GF PBT, 15% Glass Reinforced
- Ineos Styrenics Polystyrene 147F (NAFTA)
- Haynes Ultimet® alloy, plate, GMAW weld (spray)
- A. Schulman POLYBATCH™ Beige 60199 Concentrate Based In LLDPE
- American Polymers API 650-21 Polystyrene
- Dow Corning HS III HS SPRAYABLE CATALYST - CLEAR
- Fainplast Compounds PK 5510 Flexible PVC, Lead Free
- Fainplast Compounds RE 130 Rigid PVC, Extrusion
- Samyang Triel® 5652EM Thermoplastics Polyetherester Elastomer, Extrusion
Copyright © lookpolymers.com All Rights Reserved