Lucite International Diakon® CMG314V Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® CMG314V Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ISO 2039-2 |
| Ball Indentation Hardness | 185 MPa | 26800 psi | ISO 2039-1 |
| Tensile Strength | 83.0 MPa | 12000 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Vicat Softening Point | 108 °C | 226 °F | ISO 306B |
| 117 °C | 243 °F | ISO 306A | |
| Heat Distortion Temperature | 102 °C | 216 °F | ISO 75A |
| 105 °C | 221 °F | ISO 75B | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.40 % | 0.40 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)
- SolVin 367NC Polyvinyl Chloride Low Viscosity Paste
- Silberline SparkleBriteâ„¢ 190NL-PA
- A. Schulman CP842-01 Hexene Copolymer LLDPE Resin
- A. Schulman POLYBATCH™ White 8750 Concentrate Based In HDPE
- Hexcel® HexWeb® CR III 1/8-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene
- Eastman Tenite Propionate 383A2R30007 Natural, Trsp Cellulose Acetate Propionate
Copyright © lookpolymers.com All Rights Reserved