PlastxWorld DAICEL STYROL® SK50H HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | PlastxWorld, Inc. |
| Trade Name | DAICEL STYROL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastxWorld DAICEL STYROL® SK50H HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.9 MPa | 5500 psi | ASTM D638 |
| Flexural Yield Strength | 56.5 MPa | 8200 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 6.35 mm |
0.600 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | 0.5 inch; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® TR-0535-UI Hexene MDPE Rotational Molding Resin
- Latrobe Marvac 300 VIM-VAR ; 10 in. High Strength Maraging Steel
- Indorama AlphaPet Preformance® 1708HS(A) PET Resin
- Shamrock Technologies NanoFLON® P 47A Thermoplastic Grade PTFE Additive
- Borealis LR4201L Polyethylene Insulation Compound, Crosslinkable
- Dow DS6D81 Polypropylene Random Copolymer Resin
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- Cathay PA510 Renewable Engineering Polyamide
- Asahi Kasei Thermylon® NSG-240A 50% Ceramic and Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved