- Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced
Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 260 °C |
15 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 91.03 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Strength | 131.03 MPa | 19004 psi | ASTM D790 |
| Flexural Modulus | 3.897 GPa | 565.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.800 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 116.67 °C | 242.01 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PTS Trimid® N6-600 Medium Viscosity Extrusion Grade Nylon 6
- SABIC Innovative Plastics LNP Colorcomp DX98735 PC
- LATI Latamid SP1 G/50 PA 6.10, 50% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66
- SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS
- Styrolution PS 576H HIPS
- SABIC Innovative Plastics NORYL ENV150 PPE (Europe-Africa-Middle East)
- Hexcel® HexWeb® HRH-10/OX - 3/16 - 1.8 Aramid Fiber/Phenolic Resin Honeycomb
- Tra-Con Tra-Bond FS12 Fast Cure Epoxy Adhesive System
- Aaron Industries AAROPRENE® GFPC 5020 Glass Filled Polycarbonate
Copyright © lookpolymers.com All Rights Reserved